FlashForge NexPA-CF25 1000g - 3D Printing Filament
NexPA-CF25 - NexPA-CF25 is een hoogwaardig nylonfilament met 25% koolstofvezelversterking en een co-geëxtrudeerde skin-core structuur. De buitenlaag zorgt voor sterke laaghechting, terwijl de kern gehakte vezels bevat voor hoge sterkte en hittebestendigheid. Dit ontwerp verbetert de Z-as hechting, mechanische prestaties en maatvastheid en vermindert slijtage van de nozzle. Ideaal voor dunwandige, dragende en technisch sterke onderdelen.
- Gewicht: 1 kg.
- Lengte: 355,3 m.
- Diameter: 1,75 ± mm.
Dichtheid (bij 21,5 °C): 1,17 g/cm³.
Temperatuurbestendigheid: 147 °C. voor vervorming
- Spoel: 200mm Buitenste diameter & 53mm Binnenste diameter & 63mm Hoogte, In plastic
338,42 €
279,69 € excl. BTW
Goedkoopste privé verzending 6,99 €
Extern magazijn, 6 - 7 werkdagen levertijd
NexPA-CF25 is an outstanding candidate for printing parts that need to have thin walls and high mechanical property requirements. It is one type of 3D printing filament with 25% carbon fiber content and a skin-core structure. The outer ‘skin’ of the filament is a modified resin with high layer adhesion strength, and the inner core is reinforced resin containing high chopped fiber content.
Printing filaments take advantage of the general laminar flow of polymeric fluids during extrusion and maintain the stable skin-core structure even after the filament passes through the nozzle of the printer. This technology contributes to the excellent Z-axis interlayer adhesion of FDM fiber-reinforced filaments because the major layer adhesion comes from the outer shell rein without fibers.
Meanwhile, 25% chopped cabron fiber content can improve the mechanical properties and heat resistance of the printed parts.
Co-extrusion ‘skin-core’ structure
The new generation of industrial 3D printing filament features a skin-core structure. The outer 'skin' is a modified resin with high layer adhesion, and the inner core is reinforced resin containing high chopped fiber content.The co-extrusion skin-core technology has greatly increased fiber content while maintaining the toughness of the filament and thus improved the mechanical properties and heat resistance of the printed parts.
Excellent layer adhesion
The 3D printing filaments have taken advantage of the general laminar flow of polymeric fluids during the extrusion and maintain the stable skin-core structure even after the filament passes through the nozzle of the printer. Among many other fiber-reinforced filaments, Z-axis layer adhesion loss is always a common issue during printing. However, for 3D printing filaments, the Z-axis interlayer adhesion comes from the adhesion between the resin of the outer shell and this can completely avoid the layer adhesion loss.
In addition, after being extruded through the nozzle, the inner core and outer layers of the extruded filament are heated, melted and bonded together again. In this way, the adhesion between the inner and outer layers can reach the optimal level and the fibers of the inner core can effectively withstand the force from the z-axis outer layer resin. With these two advantages, the Z-axis interlayer adhesion of final parts printed with these filaments is further improved compared to parts printed with pure resin filaments.
Reducing nozzle abrasive wear
During the extrusion process, the filaments can greatly reduce the wear of the nozzle. The material that contacts the inner wall of the nozzle is made of pure resin which greatly limits the contact between the reinforcing fibers and the nozzle. At the same time, the skin-core structured filament can also avoid the contact between the reinforcing fibers of the filament and extruders or throats, which prolongs the service life of the entire extrusion parts of the 3D printer.
Printing filaments take advantage of the general laminar flow of polymeric fluids during extrusion and maintain the stable skin-core structure even after the filament passes through the nozzle of the printer. This technology contributes to the excellent Z-axis interlayer adhesion of FDM fiber-reinforced filaments because the major layer adhesion comes from the outer shell rein without fibers.
Meanwhile, 25% chopped cabron fiber content can improve the mechanical properties and heat resistance of the printed parts.
Co-extrusion ‘skin-core’ structure
The new generation of industrial 3D printing filament features a skin-core structure. The outer 'skin' is a modified resin with high layer adhesion, and the inner core is reinforced resin containing high chopped fiber content.The co-extrusion skin-core technology has greatly increased fiber content while maintaining the toughness of the filament and thus improved the mechanical properties and heat resistance of the printed parts.
Excellent layer adhesion
The 3D printing filaments have taken advantage of the general laminar flow of polymeric fluids during the extrusion and maintain the stable skin-core structure even after the filament passes through the nozzle of the printer. Among many other fiber-reinforced filaments, Z-axis layer adhesion loss is always a common issue during printing. However, for 3D printing filaments, the Z-axis interlayer adhesion comes from the adhesion between the resin of the outer shell and this can completely avoid the layer adhesion loss.
In addition, after being extruded through the nozzle, the inner core and outer layers of the extruded filament are heated, melted and bonded together again. In this way, the adhesion between the inner and outer layers can reach the optimal level and the fibers of the inner core can effectively withstand the force from the z-axis outer layer resin. With these two advantages, the Z-axis interlayer adhesion of final parts printed with these filaments is further improved compared to parts printed with pure resin filaments.
Reducing nozzle abrasive wear
During the extrusion process, the filaments can greatly reduce the wear of the nozzle. The material that contacts the inner wall of the nozzle is made of pure resin which greatly limits the contact between the reinforcing fibers and the nozzle. At the same time, the skin-core structured filament can also avoid the contact between the reinforcing fibers of the filament and extruders or throats, which prolongs the service life of the entire extrusion parts of the 3D printer.
Producent
Productnummer
3396705
Model
90009581001
EAN
6937120305392
Naar de website van de producent
Bovenstaande specificaties en vermeldingen kunnen zonder voorafgaande kennisgeving door de fabrikant worden gewijzigd. Sommige teksten kunnen automatisch of machinaal zijn gegenereerd en daardoor misleidende teksten opleveren.